Analysis of Small Pores, Cracks, Glazed Tears, Red Stains of Crystalline Iron on Glaze, and Color Differences in Patterns in Jianzhan Tire
(The products in this link are all from Jianyao Jianzhan, authentic iron body, authentic mineral glaze, without chemical glaze, shipped from the country of origin, exquisite and flawless, guaranteed authenticity) 1: There are many small pores inside the lamp, mainly caused by the air released during the firing process of the body and glaze. The pores are the result of the iron left behind during the firing process. This situation is common when Jianzhan is fired once, and the pores do not affect the integrity and daily use of the glaze surface of Jianzhan.). 2: Opening is a natural phenomenon of porcelain glaze, during which the embryo clay extends in one direction, affecting the sorting of molecules. The expansion coefficients of the embryo and clay are different, resulting in a large shrinkage rate of the glaze layer during firing and cooling.
3: The unique fertilizer rich thick glaze of the glazed tear construction lamp flows during high-temperature firing in the kiln, and some form hanging glaze on the outer wall, commonly known as "glazed tears" or the appearance of fertilizer glaze at the bottom of the lamp. If the glaze deviates, it is considered a normal display. Please purchase from us.
4: The iron red spots on the glaze are like flowers, silver hairs, or oil droplets, formed by the accumulation of high iron content during high-temperature firing, occasionally resulting in iron red spots. 5: The color difference of the pattern in the construction of the lamp belongs to high-temperature firing in the kiln, with one color when entering the kiln and ten thousand colors when leaving the kiln. Therefore, the glaze color spots and patterns are not consistent. The pictures are for reference only, and the final product shall prevail. Good ceramic works pursue a finishing effect during production and are viewed with an appreciative eye.
6: There is a slight error in the size of the handmade lamp, but it does not affect the product quality and appearance.
(The products in this link are all from Jianyao Jianzhan, authentic iron body, authentic mineral glaze, without chemical glaze, shipped from the country of origin, exquisite and flawless, guaranteed authenticity) 1: There are many small pores inside the lamp, mainly caused by the air released during the firing process of the body and glaze. The pores are the result of the iron left behind during the firing process. This situation is common when Jianzhan is fired once, and the pores do not affect the integrity and daily use of the glaze surface of Jianzhan.). 2: Opening is a natural phenomenon of porcelain glaze, during which the embryo clay extends in one direction, affecting the sorting of molecules. The expansion coefficients of the embryo and clay are different, resulting in a large shrinkage rate of the glaze layer during firing and cooling.
3: The unique fertilizer rich thick glaze of the glazed tear construction lamp flows during high-temperature firing in the kiln, and some form hanging glaze on the outer wall, commonly known as "glazed tears" or the appearance of fertilizer glaze at the bottom of the lamp. If the glaze deviates, it is considered a normal display. Please purchase from us.
4: The iron red spots on the glaze are like flowers, silver hairs, or oil droplets, formed by the accumulation of high iron content during high-temperature firing, occasionally resulting in iron red spots. 5: The color difference of the pattern in the construction of the lamp belongs to high-temperature firing in the kiln, with one color when entering the kiln and ten thousand colors when leaving the kiln. Therefore, the glaze color spots and patterns are not consistent. The pictures are for reference only, and the final product shall prevail. Good ceramic works pursue a finishing effect during production and are viewed with an appreciative eye.
6: There is a slight error in the size of the handmade lamp, but it does not affect the product quality and appearance.